Scroll to the right to view the values.
| Reference Standard
CC483K-GC UNI EN 1982 | Chemical Analysis % Chemical Composition |
||||||||||||
| Sn% | Zn% | Pb% | Fe% | Ni% | Al% | P% | Si% | Mn% | Sb% | As% | Cu% | Rest | |
| Min | 11,00 | - | - | - | - | - | - | - | - | - | - | 85,00 | - |
| Max | 13,00 | 0,50 | 0,70 | 0,20 | 2,00 | 0,01 | 0,70 | 0,01 | 0,20 | 0,15 | - | 88,50 | - |
| Casting Process and Designation | Mechanical Properties | |||
| Yield Strength Rp 0.2 N/mm² | Tensile Strength Rm N/mm² | Elongation at Break A% | Brinell Hardness HB |
|
| Sand Cast -GS | 140 | 260 | 7 | 80 |
| Shell Cast -GM | 150 | 270 | 5 | 80 |
| Sand Cast -GZ | 150 | 280 | 5 | 90 |
| Continuous Cast -GC | 150 | 300 | 6 | 90 |
Application:
Alloy generally intended for the construction of supports and bushings for hardened or chrome-plated steel shafts. Due to its high castability, it can be advantageously used in the construction of complex castings for hydraulic applications (bodies and impellers of centrifugal pumps). Used for gear wheels in combination with steel worm screws.
N.B.: For further information, please contact our Sales Office